KARATERISTIK SIFAT FISIKA DAN MEKANIKA PAPAN LAMINASI KAYU BAYUR (Pterospermum diversifolium) SEBAGAI BAHAN SUBSTITUSI PAPAN SOLID

  • Febriana Tri Wulandari Jurusan Kehutanan Universitas Mataram
  • Sitti Latifah Jurusan Kehutanan Universitas Mataram
Keywords: Bayur wood, , physical properties, mechanical properties, solid board

Abstract

Bayur wood is included in strong class III with a specific gravity ranging from 0.30-0.70 (average 0.53) and has a slightly rough texture but generally has a smooth and shiny surface. This research will look at the characteristics of bayur wood laminated boards as a substitute for solid boards. To determine the quality of the laminated board produced, it is necessary to test the physical and mechanical properties of the resulting laminated board. The method used in this study used an experimental method with an experimental design using a non-factorial Completely Randomized Design (CRD). Based on the results of the research on bayur wood laminated boards, it can be concluded that the value of the physical and mechanical properties of laminated boards has met the standards of SNI 03-2105-2006 and JAS JAS 234-2007 except for the thickness shrinkage and Modulus of Elasticity (MoE) tests. Laur weight treatment did not significantly affect all tests of physical and mechanical properties of Bajur wood laminated boards except for testing the moisture content and Modulus of Rupture (MoR). Based on the standard of wood strength class, laminated boards from Bayur wood are equivalent to wood with strength class III

Downloads

Download data is not yet available.

References

Adurrachman dan Nurwati Hadjib. 2008. Sifat Fisik dan Mekanik Kayu Lamina Campuran Kayu Mangium dan Sengon. Pusat Litbang Hasil Hutan. Jurnal Penelitian Hasil Hutan Vol. 27 No. 3, September 2009: 191-200.
Agung Faisal Ardiansyah (2017). Variasi Aksial Sifat Fisika Dan Mekanika Kayu Jati (Tectona
Grandis Linn.F.) Sumbawa Barat Skripsi. Jurusan Kehutanan Fakultas Pertanian Universitas Mataram
Darwis, Atmawi, Muhammad Y Massijaya, Naresworo Nugroho dan Eka M Alamsyah. 2014. Karakteristik Glulam dari Batang Kelapa Sawit (The Characteristics of the Laminated Board of Oil Palm Trunk). Ilmu Teknol. Kayu Tropis Vol. 12 No.2 Juli 2014.
Fandi Ade Wijaya, 2017 Variasi Arah Radial Sifat Fisika Dan Mekanika Kayu jati (Tectona Grandis Linn.F.) Sumbawa Barat Skripsi.Jurusan Kehutanan Fakultas Pertanian Universitas Mataram
Gusmawati E, 2018. Sifat Fisika dan Mekanika Papan Laminasi Berdasarkan Warna Bidang Orientasi Kayu. Program Studi Kehutanan Universitas Mataram.
Haygreen, J.G dan J.L Bowyer, 2003. Hasil Hutan dan Ilmu Kayu, Suatu Pengantar (Terjemahan Sutjipto, AH), Gadjah Mada University Press Yogyakarta.
Herawati E, Massijaya, M. Y., Nugroho N. 2008. Karakteristik Balok Laminasi dari Kayu Mangium (Acacia Mangium Wiild). Jurnal Ilmu dan Teknologi Hasil Hutan. Vol.1, Hal.1-8.
Kasmudjo. 2001. Pengantar Teknologi Hasil Hutan Bagian V Papan Tiruan Lain. Yayasan Pembina Fakultas Kehutanan. UGM. Yogyakarta.
Kollman and Kuen Zl, dalam Samad, SH 2001. Perekat dan Perekatan Kayu. Fakultas Kehutanan Universitas Lambung Mangkurat, Banjar baru.
Malik, J & Santoso, A. 2005. Keteguhan Lentur Statis Lamina dari Tiga Jenis Kayu Limbah Pembalakan Hutan Tanaman. Jurnal Penelitian Hadil Hutan. Vol.23. Hal.385-397.
Mahdavi, M., P. L. Clouston, & S. R. Arwade. 2011. Development of Laminated Bamboo Lumber: Review of Processing, Performance, and Economical Conciderations. Jurnal of Materials In Civil Engineering, Juli 2011. Halaman: 1036-1042.
Muhtariana, D. 2013. Kuantifikasi Kayu Sisa Penebangan Habis Jati Di RPH Panggung BKPH Dagangan KPH Madiun Perum Perhutani Unit II Jawa Timur. Skripsi. Departemen Manajemen Hutan, Fakultas Kehutanan. Institut Pertanian Bogor. Bogor.
Mochsin, Fadillah H dan Usman Nurhaida. 2014. Stabilitas Dimensi Berdasarkan Suhu Pengeringan dan Jenis Kayu. ISSN: 2776-1754. Jurnal Hutan Lestari Vol, 2, No 2 ( 2014).
Nugroho, Sigit. 2008. Dasar-dasar Rancangan Percobaan. UNIB Press. Bengkulu.
Purwanto, D. 2011. Pembuatan Balok dan Papan dari Limbah Industri Kayu. Balai Riset dan Standarisasi Industri Banjarbaru. Jurnal Riset Industri, Vol.5. Hal.13-20.
Widyawati, R. 2010. Kekuatan Sambungan Tegak (Butt Joint) Struktur Balok Laminasi (Glulam Beams) dari Kayu Lokal. Jurnal Rekayasa 14. 28-38.
Wulandari, F.T. 2013. Produk Papan Komposit Dengan Pemanfaatan Limbah Non Kayu. Prodi Kehutanan Faperta Unram. Jurnal Media Bina Ilmiah. Vol.7.
Wulandari, Febriana Tri. 2015. Papan Komposit; Produk Hasil Hutan yang Ramah Lingkungan. Jurnal Sangkareang Mataram. Vol. 1 No. 2.
Widiati, Kusno Yuli, Bandi Supraptono dan Arif budi Yuni Tripratono. 2018. Karakteristik Sifat Fisika dan Mekanika Kayu Lamina Kombinasi Jenis Kayu Sengon (Paraserianthes falcataria (L.) Nilsen) dan Jenis Kayu Merbau (Intsia Spp.). pISSN 2599 1205, eISSN 2599 1183. Ulin – J Hut Trop 2(2): 93-97.
Wulandari, F.T dan Sitti Latifah, 2021. Laminated board Limbah Potongan Kayu Sebagai Bahan Substitusi Kayu Solid. Laporan Hasil Penelitian PNPB anggaran 2021 Jurusan Kehutanan Universitas Mataram.
Published
2022-07-30
Section
Artikel Ilmiah
Abstract viewed = 160 times
PDF downloaded = 144 times